Poliuretano elastomer formed by the polymerization reaction of diisocyanate and active hydrogen compound, the rigid segment containing urea group composed of diisocyanate and diamine chain extender, the glass transition temperature is much higher than room temperature, and it is glassy at room temperature. Subcrystals or microcrystals form the plastic phase; flexible segments of polyether or polyester are gathered together to form the matrix or matrix of the poliuretano rubber. Because its glass transition temperature is lower than room temperature, it is called the rubber phase. The microphase separation of the poliuretano elastomer makes the poliuretano elastomer have the advantages of good wear resistance, wide range of hardness, high strength and high elongation, large load supporting capacity, good shock absorption effect and excellent oil resistance. Choosing a suitable molding and processing method can maximize the performance of poliuretano elastomers and prepare various poliuretano elastomers with excellent properties, which are widely used as plastics, rubber, fibers, adhesives and coatings, and even as functional polymer materials. Such as medical poliuretanomateriales.
1.1 Principios generales para la selección de métodos de procesamiento de conformado
(1) El proceso de moldeo consiste generalmente en fundir o deformar un compuesto polimérico en estado sólido (polvo o granulado), pasta o solución, y formar la forma deseada a través de un molde, y mantener la forma que se ha obtenido, y finalmente obtener el producto. proceso de elaboración.
(2) Flujo común de procesamiento de moldeo: “El método de formar la mezcla de compuestos poliméricos una y dos veces para producir productos; “¡El método de formación del compuesto polimérico para producir productos al mismo tiempo; â ‘¢ El método de producción de productos a partir de la mezcla de monómeros en un paso. â‘ £ Método de producción de una mezcla de oligómeros en un solo paso.
(3) Rendimiento de procesamiento y sus factores de influencia: "Estrujabilidad, en la extrusora, el barril de la máquina de inyección, los rodillos de la calandria y el molde, cuando el material se deforma por extrusión, se obtiene la forma del material y capacidad mantenida. Sus factores restrictivos: viscosidad de la masa fundida, estructura del equipo de procesamiento, reología de la masa fundida y velocidad de flujo de la masa fundida. “¡Moldeabilidad, en el proceso de moldeo bajo la acción de la máquina de inyección, extrusora y máquina de compresión, el material se deforma bajo la acción de temperatura y presión y la capacidad de ser moldeado en el molde. Sus factores restrictivos: reología, propiedades térmicas y otras propiedades físicas y mecánicas y reactividad química de los compuestos poliméricos. â ‘¢ Extensibilidad, en calandrado o estirado, el material se deforma por calandrado o estirado en una o dos direcciones. Sus factores restrictivos: la plasticidad del material y el efecto de endurecimiento por deformación. â ‘£ Hilabilidad, la boquilla durante el moldeo por extrusión, la capacidad del material para formar fibras sólidas continuas a través del moldeo. Sus factores restrictivos: reología, viscosidad y resistencia de la masa fundida, estabilidad térmica y estabilidad química.
1.2 Principios generales para la selección de métodos de moldeo y procesamiento parapoliuretanoelastómeros
Poliuretano elastomer molding processing system is divided into liquid system and solid system. On the basis of the rapid polymerization reaction of diisocyanate and active hydrogen compound, the molding processing method is conducive to the microphase separation of the poliuretano elastomer. , Liquid system, poliuretano casting glue can be processed by casting (manual casting, centrifugal casting and vacuum casting), reaction injection molding, spraying, knife coating, roller coating, laminating, laminating, bonding, vulcanizing, pasting and rubbing ; Solid system, poliuretano compound rubber can be vulcanized and laminated with mold, poliuretano thermoplastic can be used with thermoplastic, hot injection, calendering, blow molding, spinning and lamination.
1.3 El principio de coincidencia de tipos básicos y métodos de procesamiento de moldeo
PoliuretanoEl elastómero es un polímero alto entre plástico y caucho en términos de su módulo. Incluye principalmentepoliuretano compound rubber, poliuretano cast rubber, poliuretano water emulsion and poliuretano thermoplastic. Poliuretano leather, poliuretano adhesives, poliuretano coatings, poliuretano compounds, poliuretano casting glues, poliuretano fibers, poliuretano water emulsions and poliuretano thermoplastics are all derived from the above four types of glue. The molding and processing methods of poliuretano compound rubber, poliuretano water emulsion and poliuretano thermoplastic generally belong to the molding processing methods of rubber, coatings and plastics.
1.4 The use of poliuretano elastomers and the matching principle of production continuity and molding processing methods
Poliuretano elastomer molding and processing methods are matched with the use of poliuretano elastomers, taking into account the continuity of production. For example, poliuretano leather molding methods usually use poliuretano casting adhesive or foaming layer, poliuretano water emulsion and poliuretano thermoplastic as the surface layer; also available Poliuretano thermoplastic and poliuretano water emulsion are used as leather separately, which are based on the basic rubber molding processing method, supplemented by foam molding processing, usually calender molding processing method is selected. Poliuretano paving materials are made of poliuretano casting glue, mainly due to the large product shape and low precision requirements. Medical poliuretano materials have good chemical stability, tissue compatibility, and resistance to biological aging, so the molding process uses dip coating, pouring and coating methods.